IMI 230 Ti Alloy

Data Table for: Steel Grades : Ti Alloy : IMI 230 Ti Alloy

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce IMI 230 Ti Alloy specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • IMI 230 Ti Alloy
  • IMI 230 Ti Alloy
  • IMI 230 Ti Alloy
  • IMI 230 Ti Alloy
  • IMI 230 Ti Alloy
  • IMI 230 Ti Alloy
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyIMI 230 plate,IMI 230 Round Bar,IMI 230 forgings,IMI 230 suppliers, IMI 230 Stock,IMI 230 sheet, IMI 230 flat bar, IMI 230 pipe,IMI 230 tube,IMI 230 mould,IMI 230 round ingot,IMI 230 cold-rolled steel,IMI 230 coil,IMI 230 strap steel,IMI 230 hot-rolled steel,IMI 230 medium plate, IMI 230 heavy plate,IMI 230 shapped bar,IMI 230 hexahedral bar,IMI 230,IMI 230 slab ingot,IMI 230 slab,IMI 230 price,IMI 230 square bar,IMI 230 square steel,IMI 230 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of IMI 230.

 

IMI 230 Ti Alloy

Our advantages

IMI 230 properties and heat treatment forged piece, Including IMI 230 application and specifications, We have all specifications,Including IMI 230 steel plate, IMI 230 sheet, IMI 230 square steel, IMI 230 flat bar,IMI 230 round bar,IMI 230 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the IMI 230 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade IMI 230 and Standards

Titanium IMI 230 (Ti-2.5Cu)
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy

Material Notes: Annealed; Aging increases Strength

 

Physical Properties Metric English Comments
Density 4.56 g/cc 0.165 lb/in³
 
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 620 MPa 89900 psi
Tensile Strength, Yield 480 MPa 69600 psi
Elongation at Break 24.0 % 24.0 %
Modulus of Elasticity 105 GPa 15200 ksi
Poissons Ratio 0.310 0.310 Typical for alpha titanium alloy.
Fatigue Strength 280 MPa
@# of Cycles 1.00e+7
40600 psi
@# of Cycles 1.00e+7
Shear Modulus 40.1 GPa 5820 ksi Calculated from typical values.
 
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000650 ohm-cm 0.0000650 ohm-cm
 
Thermal Properties Metric English Comments
CTE, linear 9.02 µm/m-°C
@Temperature 20.0 - 100 °C
5.01 µin/in-°F
@Temperature 68.0 - 212 °F
  9.10 µm/m-°C
@Temperature 20.0 - 300 °C
5.06 µin/in-°F
@Temperature 68.0 - 572 °F
average
  9.46 µm/m-°C
@Temperature 20.0 - 600 °C
5.26 µin/in-°F
@Temperature 68.0 - 1110 °F
average
Specific Heat Capacity 0.525 J/g-°C 0.125 BTU/lb-°F Typical value for titanium alloys.
Thermal Conductivity 13.0 W/m-K 90.2 BTU-in/hr-ft²-°F
Beta Transus 895 °C 1640 °F
 
Component Elements Properties Metric English Comments
Carbon, C <= 0.0800 % <= 0.0800 %
Copper, Cu 2.00 - 3.00 % 2.00 - 3.00 %
Hydrogen, H <= 0.0100 % <= 0.0100 %
Iron, Fe <= 0.200 % <= 0.200 %
Nitrogen, N <= 0.0500 % <= 0.0500 %
Other, total <= 0.400 % <= 0.400 %
Oxygen, O <= 0.200 % <= 0.200 %
Titanium, Ti 96.06 - 98.0 % 96.06 - 98.0 % As Balance; Elemental Compostions per ASTM B265

 

Users viewing this material also viewed the following:
Titanium Ti-6Al-2Sn-4Zr-2Mo-0.1Si; Duplex Annealed
Titanium Ti-3Al-2.5V (Grade 9), alpha annealed
Titanium IMI 230 (Ti-2.5Cu), aged
Titanium Ti-5Al-2.5Sn (Grade 6)
Titanium 11 (Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si)

MTA231 / 14121




Machining performance

Download IMI 230 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:IMI 230 steel plate, IMI 230 sheet, IMI 230 square steel, IMI 230 flat bar,IMI 230 round bar,IMI 230 forgings

 
 

关闭提示 关闭

 

确 认 取 消

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:IMI 230

Previous pageTi-3Al-2.5V Grade 9 Ti Alloy
Next page:Ti-621/0.8 Ti Alloy