Ti-15V-3Cr-3Sn-2Al Ti Alloy

Data Table for: Steel Grades : Ti Alloy : Ti-15V-3Cr-3Sn-2Al Ti Alloy

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce Ti-15V-3Cr-3Sn-2Al Ti Alloy specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • Ti-15V-3Cr-3Sn-2Al Ti Alloy
  • Ti-15V-3Cr-3Sn-2Al Ti Alloy
  • Ti-15V-3Cr-3Sn-2Al Ti Alloy
  • Ti-15V-3Cr-3Sn-2Al Ti Alloy
  • Ti-15V-3Cr-3Sn-2Al Ti Alloy
  • Ti-15V-3Cr-3Sn-2Al Ti Alloy
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi-15V-3Cr-3Sn-2Al plate,Ti-15V-3Cr-3Sn-2Al Round Bar,Ti-15V-3Cr-3Sn-2Al forgings,Ti-15V-3Cr-3Sn-2Al suppliers, Ti-15V-3Cr-3Sn-2Al Stock,Ti-15V-3Cr-3Sn-2Al sheet, Ti-15V-3Cr-3Sn-2Al flat bar, Ti-15V-3Cr-3Sn-2Al pipe,Ti-15V-3Cr-3Sn-2Al tube,Ti-15V-3Cr-3Sn-2Al mould,Ti-15V-3Cr-3Sn-2Al round ingot,Ti-15V-3Cr-3Sn-2Al cold-rolled steel,Ti-15V-3Cr-3Sn-2Al coil,Ti-15V-3Cr-3Sn-2Al strap steel,Ti-15V-3Cr-3Sn-2Al hot-rolled steel,Ti-15V-3Cr-3Sn-2Al medium plate, Ti-15V-3Cr-3Sn-2Al heavy plate,Ti-15V-3Cr-3Sn-2Al shapped bar,Ti-15V-3Cr-3Sn-2Al hexahedral bar,Ti-15V-3Cr-3Sn-2Al,Ti-15V-3Cr-3Sn-2Al slab ingot,Ti-15V-3Cr-3Sn-2Al slab,Ti-15V-3Cr-3Sn-2Al price,Ti-15V-3Cr-3Sn-2Al square bar,Ti-15V-3Cr-3Sn-2Al square steel,Ti-15V-3Cr-3Sn-2Al wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti-15V-3Cr-3Sn-2Al.

 

Ti-15V-3Cr-3Sn-2Al Ti Alloy

Our advantages

Ti-15V-3Cr-3Sn-2Al properties and heat treatment forged piece, Including Ti-15V-3Cr-3Sn-2Al application and specifications, We have all specifications,Including Ti-15V-3Cr-3Sn-2Al steel plate, Ti-15V-3Cr-3Sn-2Al sheet, Ti-15V-3Cr-3Sn-2Al square steel, Ti-15V-3Cr-3Sn-2Al flat bar,Ti-15V-3Cr-3Sn-2Al round bar,Ti-15V-3Cr-3Sn-2Al forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti-15V-3Cr-3Sn-2Al has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti-15V-3Cr-3Sn-2Al and Standards

 

Physical Properties Metric English Comments
Density 4.78 g/cc 0.173 lb/in³ Typical
 
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1300 MPa 189000 psi Typical
Tensile Strength, Yield 1210 MPa
@Strain 0.200 %
175000 psi
@Strain 0.200 %
Typical
Elongation at Break 9.00 % 9.00 % Typical
Modulus of Elasticity 107 GPa 15500 ksi Typical
 
Thermal Properties Metric English Comments
CTE, linear 8.60 µm/m-°C
@Temperature 20.0 °C
4.78 µin/in-°F
@Temperature 68.0 °F
  9.20 µm/m-°C
@Temperature 20.0 - 250 °C
5.11 µin/in-°F
@Temperature 68.0 - 482 °F
  9.90 µm/m-°C
@Temperature 20.0 - 500 °C
5.50 µin/in-°F
@Temperature 68.0 - 932 °F
Specific Heat Capacity 0.500 J/g-°C 0.120 BTU/lb-°F
Thermal Conductivity 8.30 W/m-K 57.6 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 288 °C 550 °F
Beta Transus 760 °C 1400 °F
 
Component Elements Properties Metric English Comments
Aluminum, Al 2.50 - 3.50 % 2.50 - 3.50 %
Carbon, C <= 0.050 % <= 0.050 %
Chromium, Cr 2.50 - 3.50 % 2.50 - 3.50 %
Hydrogen, H <= 0.015 % <= 0.015 %
Iron, Fe <= 0.25 % <= 0.25 %
Nitrogen, N <= 0.050 % <= 0.050 %
Oxygen, O <= 0.13 % <= 0.13 %
Tin, Sn 2.50 - 3.50 % 2.50 - 3.50 %
Titanium, Ti 72.6 - 78.5 % 72.6 - 78.5 % Calculated as remainder
Vanadium, V 14.0 - 16.0 % 14.0 - 16.0 %

 




Machining performance

Download Ti-15V-3Cr-3Sn-2Al the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti-15V-3Cr-3Sn-2Al steel plate, Ti-15V-3Cr-3Sn-2Al sheet, Ti-15V-3Cr-3Sn-2Al square steel, Ti-15V-3Cr-3Sn-2Al flat bar,Ti-15V-3Cr-3Sn-2Al round bar,Ti-15V-3Cr-3Sn-2Al forgings

 
 

关闭提示 关闭

 

确 认 取 消

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:Ti-15V-3Cr-3Sn-2Al Ti Alloy

Previous pageHM21A-T81 Ti Alloy
Next page:UNS R58030 Ti Alloy