Ti-5Al-2.5Sn Grade 6 Ti Alloy

Data Table for: Steel Grades : Ti Alloy : Ti-5Al-2.5Sn Grade 6 Ti Alloy

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce Ti-5Al-2.5Sn Grade 6 Ti Alloy specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • Ti-5Al-2.5Sn Grade 6 Ti Alloy
  • Ti-5Al-2.5Sn Grade 6 Ti Alloy
  • Ti-5Al-2.5Sn Grade 6 Ti Alloy
  • Ti-5Al-2.5Sn Grade 6 Ti Alloy
  • Ti-5Al-2.5Sn Grade 6 Ti Alloy
  • Ti-5Al-2.5Sn Grade 6 Ti Alloy
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi-5Al-2.5Sn Grade 6 plate,Ti-5Al-2.5Sn Grade 6 Round Bar,Ti-5Al-2.5Sn Grade 6 forgings,Ti-5Al-2.5Sn Grade 6 suppliers, Ti-5Al-2.5Sn Grade 6 Stock,Ti-5Al-2.5Sn Grade 6 sheet, Ti-5Al-2.5Sn Grade 6 flat bar, Ti-5Al-2.5Sn Grade 6 pipe,Ti-5Al-2.5Sn Grade 6 tube,Ti-5Al-2.5Sn Grade 6 mould,Ti-5Al-2.5Sn Grade 6 round ingot,Ti-5Al-2.5Sn Grade 6 cold-rolled steel,Ti-5Al-2.5Sn Grade 6 coil,Ti-5Al-2.5Sn Grade 6 strap steel,Ti-5Al-2.5Sn Grade 6 hot-rolled steel,Ti-5Al-2.5Sn Grade 6 medium plate, Ti-5Al-2.5Sn Grade 6 heavy plate,Ti-5Al-2.5Sn Grade 6 shapped bar,Ti-5Al-2.5Sn Grade 6 hexahedral bar,Ti-5Al-2.5Sn Grade 6,Ti-5Al-2.5Sn Grade 6 slab ingot,Ti-5Al-2.5Sn Grade 6 slab,Ti-5Al-2.5Sn Grade 6 price,Ti-5Al-2.5Sn Grade 6 square bar,Ti-5Al-2.5Sn Grade 6 square steel,Ti-5Al-2.5Sn Grade 6 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti-5Al-2.5Sn Grade 6.

 

Ti-5Al-2.5Sn Grade 6 Ti Alloy

Our advantages

Ti-5Al-2.5Sn Grade 6 properties and heat treatment forged piece, Including Ti-5Al-2.5Sn Grade 6 application and specifications, We have all specifications,Including Ti-5Al-2.5Sn Grade 6 steel plate, Ti-5Al-2.5Sn Grade 6 sheet, Ti-5Al-2.5Sn Grade 6 square steel, Ti-5Al-2.5Sn Grade 6 flat bar,Ti-5Al-2.5Sn Grade 6 round bar,Ti-5Al-2.5Sn Grade 6 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti-5Al-2.5Sn Grade 6 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti-5Al-2.5Sn Grade 6 and Standards

Titanium Ti-5Al-2.5Sn (Grade 6)

Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy

Material Notes: 1 other heat treatment of this alloy is in MatWeb.

Key Words: UNS R54520; Ti-5-2.5

 

Physical Properties Metric English Comments
Density 4.48 g/cc 0.162 lb/in³
 
Mechanical Properties Metric English Comments
Hardness, Brinell 320 320
Hardness, Knoop 363 363 Estimated from Rockwell C.
Hardness, Rockwell C 36 36
Hardness, Vickers 349 349 Estimated from Rockwell C.
Tensile Strength, Ultimate 861 MPa 125000 psi
Tensile Strength, Yield 827 MPa 120000 psi
Elongation at Break 15.0 % 15.0 %
Modulus of Elasticity 110 - 125 GPa 16000 - 18100 ksi
Compressive Yield Strength 830 MPa 120000 psi
Notched Tensile Strength 1240 MPa 180000 psi Kt (stress concentration factor) = 6.5
Ultimate Bearing Strength 1760 MPa 255000 psi e/D = 2
Bearing Yield Strength 1340 MPa 194000 psi e/D = 2
Poissons Ratio 0.310 0.310 Typical for alpha titanium alloy.
Charpy Impact 24.0 J 17.7 ft-lb V-notch
Fatigue Strength 290 MPa
@# of Cycles 1.00e+7
42100 psi
@# of Cycles 1.00e+7
Kt (stress concentration factor) = 2.4
  380 MPa
@# of Cycles 1.00e+7
55100 psi
@# of Cycles 1.00e+7
unnotched
  390 MPa
@# of Cycles 100000
56600 psi
@# of Cycles 100000
Kt (stress concentration factor) = 2.4
  440 MPa
@# of Cycles 1.00e+6
63800 psi
@# of Cycles 1.00e+6
unnotched
  530 MPa
@# of Cycles 100000
76900 psi
@# of Cycles 100000
Unnotched
Fracture Toughness 33.0 MPa-m½ 30.0 ksi-in½ K(ISCC)
  96.0 MPa-m½ 87.4 ksi-in½ K(IC)
Shear Modulus 48.0 GPa 6960 ksi
Shear Strength 520 MPa 75400 psi Ultimate shear strength
 
Electrical Properties Metric English Comments
Electrical Resistivity 0.000160 ohm-cm 0.000160 ohm-cm
 
Thermal Properties Metric English Comments
CTE, linear 9.40 µm/m-°C
@Temperature 0.000 - 100 °C
5.22 µin/in-°F
@Temperature 32.0 - 212 °F
  9.50 µm/m-°C
@Temperature 0.000 - 315 °C
5.28 µin/in-°F
@Temperature 32.0 - 599 °F
average; unspecified heat treatment.
  9.70 µm/m-°C
@Temperature 0.000 - 650 °C
5.39 µin/in-°F
@Temperature 32.0 - 1200 °F
average
Specific Heat Capacity 0.530 J/g-°C 0.127 BTU/lb-°F 0.674 J/g-ºC at 315ºC
Thermal Conductivity 7.80 W/m-K 54.1 BTU-in/hr-ft²-°F 10.9 W/m-ºC at 315ºC
Melting Point <= 1590 °C <= 2890 °F Liquidus
Liquidus 1590 °C 2890 °F
Beta Transus 1040 - 1090 °C 1900 - 1990 °F
 
Component Elements Properties Metric English Comments
Aluminum, Al 4.00 - 6.00 % 4.00 - 6.00 %
Carbon, C <= 0.100 % <= 0.100 %
Hydrogen, H <= 0.0150 % <= 0.0150 %
Iron, Fe <= 0.500 % <= 0.500 %
Nitrogen, N <= 0.0300 % <= 0.0300 %
Other, each <= 0.0500 % <= 0.0500 %
Other, total <= 0.300 % <= 0.300 %
Oxygen, O <= 0.200 % <= 0.200 %
Tin, Sn 2.00 - 3.00 % 2.00 - 3.00 %
Titanium, Ti 89.855 - 94.0 % 89.855 - 94.0 % As Balance; Elemental Compostions per ASTM B265

 

Users viewing this material also viewed the following:
Titanium Ti-5Al-2.5Sn, ELI, Annealed
Titanium Ti-3Al-2.5V (Grade 9), alpha annealed
Titanium Ti-6Al-2Sn-4Zr-2Mo-0.1Si; Duplex Annealed
Titanium, Ti
Titanium Ti-6Al-4V (Grade 5), Annealed

MTA520 / 14127




Machining performance

Download Ti-5Al-2.5Sn Grade 6 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti-5Al-2.5Sn Grade 6 steel plate, Ti-5Al-2.5Sn Grade 6 sheet, Ti-5Al-2.5Sn Grade 6 square steel, Ti-5Al-2.5Sn Grade 6 flat bar,Ti-5Al-2.5Sn Grade 6 round bar,Ti-5Al-2.5Sn Grade 6 forgings

 
 

关闭提示 关闭

 

确 认 取 消

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:Ti-5Al-2.5Sn Grade

Previous pageTi-5Al-2Zr-2Mo-0.25Si Ti Alloy
Next page:Ti-3Al-2.5V Grade 9 Ti Alloy