Ti-5Mo-5V-2Cr-3Al Ti Alloy

Data Table for: Steel Grades : Ti Alloy : Ti-5Mo-5V-2Cr-3Al Ti Alloy

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce Ti-5Mo-5V-2Cr-3Al Ti Alloy specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • Ti-5Mo-5V-2Cr-3Al Ti Alloy
  • Ti-5Mo-5V-2Cr-3Al Ti Alloy
  • Ti-5Mo-5V-2Cr-3Al Ti Alloy
  • Ti-5Mo-5V-2Cr-3Al Ti Alloy
  • Ti-5Mo-5V-2Cr-3Al Ti Alloy
  • Ti-5Mo-5V-2Cr-3Al Ti Alloy
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi-5Mo-5V-2Cr-3Al plate,Ti-5Mo-5V-2Cr-3Al Round Bar,Ti-5Mo-5V-2Cr-3Al forgings,Ti-5Mo-5V-2Cr-3Al suppliers, Ti-5Mo-5V-2Cr-3Al Stock,Ti-5Mo-5V-2Cr-3Al sheet, Ti-5Mo-5V-2Cr-3Al flat bar, Ti-5Mo-5V-2Cr-3Al pipe,Ti-5Mo-5V-2Cr-3Al tube,Ti-5Mo-5V-2Cr-3Al mould,Ti-5Mo-5V-2Cr-3Al round ingot,Ti-5Mo-5V-2Cr-3Al cold-rolled steel,Ti-5Mo-5V-2Cr-3Al coil,Ti-5Mo-5V-2Cr-3Al strap steel,Ti-5Mo-5V-2Cr-3Al hot-rolled steel,Ti-5Mo-5V-2Cr-3Al medium plate, Ti-5Mo-5V-2Cr-3Al heavy plate,Ti-5Mo-5V-2Cr-3Al shapped bar,Ti-5Mo-5V-2Cr-3Al hexahedral bar,Ti-5Mo-5V-2Cr-3Al,Ti-5Mo-5V-2Cr-3Al slab ingot,Ti-5Mo-5V-2Cr-3Al slab,Ti-5Mo-5V-2Cr-3Al price,Ti-5Mo-5V-2Cr-3Al square bar,Ti-5Mo-5V-2Cr-3Al square steel,Ti-5Mo-5V-2Cr-3Al wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti-5Mo-5V-2Cr-3Al.

 

Ti-5Mo-5V-2Cr-3Al Ti Alloy

Our advantages

Ti-5Mo-5V-2Cr-3Al properties and heat treatment forged piece, Including Ti-5Mo-5V-2Cr-3Al application and specifications, We have all specifications,Including Ti-5Mo-5V-2Cr-3Al steel plate, Ti-5Mo-5V-2Cr-3Al sheet, Ti-5Mo-5V-2Cr-3Al square steel, Ti-5Mo-5V-2Cr-3Al flat bar,Ti-5Mo-5V-2Cr-3Al round bar,Ti-5Mo-5V-2Cr-3Al forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti-5Mo-5V-2Cr-3Al has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti-5Mo-5V-2Cr-3Al and Standards

Titanium Ti-5-5-2-3 (Ti-5Mo-5V-2Cr-3Al), 12 mm Rod, Aged
Categories: Metal; Nonferrous Metal; Titanium Alloy; Beta Titanium Alloy

Material Notes: Relative to Ti-10V-2Fe-3Al. Characterized by cold formable and weldable high strength Ti alloy, in high area reduction and high fracture toughness KIC.

Applications:

Bars for deep well strings in the petroleum industry
Rods diameter 8-20 mm for high strength bolts
Near net shape forging application
Thick wall vessel
Ultra high velocity centrifugal rotor
Information provided by MarkeTech International.

 

Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1228 MPa 178100 psi Aged Condition D
  1385 MPa 200900 psi Aged Condition C
  1410 MPa 205000 psi Aged Condition B
  1533 MPa 222300 psi Aged Condition A
Elongation at Break 8.80 % 8.80 % Aged Condition A
  13.5 % 13.5 % Aged Condition B
  13.5 % 13.5 % Aged Condition C
  15.5 % 15.5 % Aged Condition D
Reduction of Area 35.0 % 35.0 % Aged Condition A
  61.0 % 61.0 % Aged Condition B
  61.0 % 61.0 % Aged Condition C
  69.0 % 69.0 % Aged Condition D
 
Component Elements Properties Metric English Comments
Aluminum, Al 3.0 % 3.0 %
Chromium, Cr 2.0 % 2.0 %
Molybdenum, Mo 5.0 % 5.0 %
Titanium, Ti 85.0 % 85.0 %
Vanadium, V 5.0 % 5.0 %

 

Users viewing this material also viewed the following:
Titanium Ti-5-5-2-3 (Ti-5Mo-5V-2Cr-3Al), 60 mm Bar, Aged
Overview of materials for Beta Titanium Alloy
Ti15Mo5Zr3Al ß titanium alloy
Titanium, Ti
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) Solution Treated 850°C (1560°F)

MTB026A / 14150




Machining performance

Download Ti-5Mo-5V-2Cr-3Al the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti-5Mo-5V-2Cr-3Al steel plate, Ti-5Mo-5V-2Cr-3Al sheet, Ti-5Mo-5V-2Cr-3Al square steel, Ti-5Mo-5V-2Cr-3Al flat bar,Ti-5Mo-5V-2Cr-3Al round bar,Ti-5Mo-5V-2Cr-3Al forgings

 
 

关闭提示 关闭

 

确 认 取 消

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:Ti-5Mo-5V-2Cr-3Al Ti

Previous pageUNS R58030 Ti Alloy
Next page:Ti-5-5-2-3 Ti Alloy