Ti30Nb Ti Alloy

Data Table for: Steel Grades : Ti Alloy : Ti30Nb Ti Alloy

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce Ti30Nb Ti Alloy specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • Ti30Nb Ti Alloy
  • Ti30Nb Ti Alloy
  • Ti30Nb Ti Alloy
  • Ti30Nb Ti Alloy
  • Ti30Nb Ti Alloy
  • Ti30Nb Ti Alloy
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi30Nb plate,Ti30Nb Round Bar,Ti30Nb forgings,Ti30Nb suppliers, Ti30Nb Stock,Ti30Nb sheet, Ti30Nb flat bar, Ti30Nb pipe,Ti30Nb tube,Ti30Nb mould,Ti30Nb round ingot,Ti30Nb cold-rolled steel,Ti30Nb coil,Ti30Nb strap steel,Ti30Nb hot-rolled steel,Ti30Nb medium plate, Ti30Nb heavy plate,Ti30Nb shapped bar,Ti30Nb hexahedral bar,Ti30Nb,Ti30Nb slab ingot,Ti30Nb slab,Ti30Nb price,Ti30Nb square bar,Ti30Nb square steel,Ti30Nb wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti30Nb.

 

Ti30Nb Ti Alloy

Our advantages

Ti30Nb properties and heat treatment forged piece, Including Ti30Nb application and specifications, We have all specifications,Including Ti30Nb steel plate, Ti30Nb sheet, Ti30Nb square steel, Ti30Nb flat bar,Ti30Nb round bar,Ti30Nb forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti30Nb has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti30Nb and Standards

Ti30Nb ß titanium alloy
Categories: Metal; Nonferrous Metal; Titanium Alloy; Beta Titanium Alloy

Key Words: medical, surgical

 

Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 700 MPa 102000 psi as rolled
Tensile Strength, Yield 500 MPa 72500 psi as rolled
Elongation at Break 20.0 % 20.0 % as rolled
Reduction of Area 60.0 % 60.0 % as rolled
Modulus of Elasticity 70.0 GPa 10200 ksi As rolled
 
Component Elements Properties Metric English Comments
Niobium, Nb (Columbium, Cb) 30.0 % 30.0 %
Titanium, Ti 70.0 % 70.0 %

 

Users viewing this material also viewed the following:
Ti30Ta ß titanium alloy
Ti15Mo5Zr3Al ß titanium alloy
Overview of materials for Beta Titanium Alloy
Titanium, Ti
Ti12Mo5Zr5Sn ß titanium alloy

MMEDIC28 / 12404




Machining performance

Download Ti30Nb the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti30Nb steel plate, Ti30Nb sheet, Ti30Nb square steel, Ti30Nb flat bar,Ti30Nb round bar,Ti30Nb forgings

 
 

关闭提示 关闭

 

确 认 取 消

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:Ti30Nb Ti

Previous pageTi30Ta Ti Alloy
Next page:Ti12Mo5Zr5Sn Ti Alloy