AISI 1330
Data Table for: Steel Grades : Alloy Steel : AISI 1330
Chemical composition(mass fraction)(wt.%)
Mechanical Properties
- Quantity
- Value
- Unit
- Young's modulus
- Tensile strength
- Elongation
- Fatigue
- Yield strength
- 200000 - 200000
- 650 - 880
- 8 - 25
- 275 - 275
- 350 - 550
- MPa
- MPa
- %
- MPa
- MPa
Physical Properties
- Quantity
- Value
- Unit
- Thermal expansion
- Thermal conductivity
- Specific heat
- Melting temperature
- Density
- Resistivity
- 10 - 10
- 25 - 25
- 460 - 460
- 1450 - 1510
- 7700 - 7700
- 0.55 - 0.55
- e-6/K
- W/m.K
- J/kg.K
- °C
- kg/m3
- Ohm.mm2/m
Heat Treatment:
Annealing |
Quenching |
Tempering |
Normalizing |
Q & T |
√ |
√ |
√ |
√ |
√ |
Can produce AISI 1330 specifications and size
- Steel grade
- Specification
- Processing range(mm)
- AISI 1330
- AISI 1330
- AISI 1330
- AISI 1330
- AISI 1330
- AISI 1330
- Φ1 to Φ2000
- 10 to 1000
- 0.08 to 800(T)*10 to 1500(W)*Long
- Pipe/tube/slugs/donuts/cubes/other shapes
- OD: Φ4-410; WT: 1-35 mm
- THK:0.1mm Width:1500mm
Description
| Category | Steel |
| Class | Alloy steel |
| Type | Standard |
| Common Names | Manganese steel |
| Designations |
Germany: DIN 1.1165 Japan: JIS SCMn 2 , JIS SMn 1 H United States: ASTM A322 , ASTM A331 , ASTM A519 , MIL SPEC MIL-S-16974 , SAE J404 , SAE J412 , SAE J770 , UNS G13300 |
Composition
| Element | Weight % |
| C | 0.28-0.33 |
| Mn | 1.60-1.90 |
| P | 0.035 (max) |
| S | 0.04 (max) |
| Si | 0.15-0.30 |
Mechanical Properties
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Density (×1000 kg/m3) | 7.7-8.03 | 25 | |
| Poisson's Ratio | 0.27-0.30 | 25 | |
| Elastic Modulus (GPa) | 190-210 | 25 | |
| Tensile Strength (Mpa) | 1158 | 25 | oil quenched, fine grained, tempered at 425°C more |
| Yield Strength (Mpa) | 1034 | ||
| Elongation (%) | 15 | ||
| Reduction in Area (%) | 53 | ||
| Hardness (HB) | 335 | 25 | oil quenched, fine grained, tempered at 425°C more |