Home » Steel Grades > Stainless Steel > 17-4PH

Category

Contact us

17-4PH

Data Table for: Steel Grades : Stainless Steel : 17-4PH

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce 17-4PH specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • 17-4PH
  • 17-4PH
  • 17-4PH
  • 17-4PH
  • 17-4PH
  • 17-4PH
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

TYPICAL ANALYSIS

 

         

C.

Mn.

P.

S.

Si.

Cr.

Ni.

Cu.

Nb.+Ta..

0.07%
max.

1.00%
max.

0.04%
max.

0.03%
max.

1.00%
max.

15.00-
17.50%

3.00-
5.00%

3.00-
5.00%

0.15-
0.45%

Solution Treatments.
As supplied 17-4PH is usuall in the solution treated condition (Condition A). It can be heat treated at different temperatures to offer a wide range of properties. (We also hold stock in H1150+H1150, and annealed block).

Condition 

  Hardening 

  Hardening 

Type of Cooling 

Hardness

 

Temperature

Time

 

  Brinell 

  Rockwell C 

A

1038°C

1/2

  Oil/Air (to below 32°C)  

  363 max. 

39 max.

H900

480°C

1

Air

420

44

H925

495°C

4

Air

409

42

H1025

550°C

4

Air 

352

38

H1075

580°C

4

Air

341

36

H1100

595°C

4

Air

332

35

H1150

621°C

4

Air

311

33

 
 H1150+H1150 


760°C

760°C


4
followed by
4


Air

Air




302




33


H1150-M


760°C

620°C


2
followed by
4


Air

Air




277




27

Typical Mechanical Properties (longitudinal)

 

A

H900

H925

H1025

H1075

H1100

H1150

    H1150+  
H1150

  H1150M  
 

Tensile Strength
N/mm2

 1034  

   1380   

    1310    

     1170   

    1140   

    1035   

    1000   

  965 

860

0.2% YS
N/mm2

760

1275

1200

1140

1035

930

860

760

585

Reduction of Area     
%

30-60

50

54

56

58

58

60

60

68

Elongation
%

6-15

14

14

15

16

17

19

20

22

Charpy Impact
J

-

20

34

47

54

61

68

108

135

Corrosion Resistance
17-4PH stainless steel has excellent corrosion resistance. Corrosion tests and service experience have shown that in all aged conditions it is superior to standard hardenable stainless grades such as 420, 431 and 410. Its corrosion resistance is comparable to grade 304 Stainless.

Welding
Arc and resistance welding processes used on standard grades of stainless steel are applicable to 17-4PH stainless steel. The low hardness enables sections, up to 100mm, to be welded without requiring pre heating.

Fabrication
17-4PH Condition is suitable for limited cold forming, H1100, H1150 and overaged conditions are more suitable when severe cold forming is required.

Machining
17-4PH Condition has machining characteristics similar to stainless grades 302, 304 and 410. The high hardness and strength in Condition H900 is the most difficult to machine and the material should be machined at 60% of the rate which is used for Condition A.

Nitriding
To increase the resistance to surface wear, with a slight decrease in corrosion resistance, 17-4PH stainless steel can be nitrided. An approximate hardness of 64/67HRc can be achieved, with a surface hardness depth of up to 0.15mm when nitrided at 540°C, while still maintaining a high core strength.

Company Instoduction:Sichuan Changcheng Special Steel Limited Liability
Company of Pan Steel Group(hereinafter referred to as PCSSC) Iocates in Jiangyou City,Sichuan Province,which former name is Changcheng Steel
Factory of Metallurgical Industry.It's built up in the year of 1965 and put into production in 1972.PCSSC has become one of the large core enterprises in Sichuan province and the important research and manufacture
base for special steel of China.In 1994,Changcheng special Steel Corporation ,the shareholding subsidiary of PCSSC has been listed on Shenzhen Stock Exchange.On June,2004,Pan steel Group reformed Changcheng Special Steel Company formally,and formed Sichuan Changcheng Special Steel
Limited Liability Company of Pan Steel Group.
At present,PCSSC has the annual production capacity to turn out 650,000
tons of special steel and 700,000 tons of finished steel products.It can supply users with 12 kinds of qualitative special steel and metal products
more than 350 grades,over 5000 dimensions on the international or national standard.The products can be widely used in all aspects of aviation,aerospace,shipbuilding,military industry,nuclear power and transportation,machine,petrochemical,medical instruments and so on.And sold to all of the country and exported into USA,Europe and Southeast Asia,etc.Some 34 products have awarded the title of the
National,Ministerial and Provincial level high-quality products.Also,product quality as cold-work mould steel has reached international level.After more than forty years development,PCSSC has grwn
into the important national special steel research and production base and military industry supporting enterprise and become irreplaceable imporyant force in the domains of national defense industry,aviation,aerospace,navigation and nuclear power.
Thereto,top-end products as titanium products and nuclear power tubes have strong market competitions and formed a new economic grow point.PCSSC is one of the three main military products and super alloyed steel production bases of China,which is on a par with the Northeast Special Steel and Special Steel of Bao Steel.It makes great contribution to insist
on self reliance,speed up national befense modern construction,to enhance our capability of independent innovation and insist on self-development to push forward nationalizing major equipment construction.
PCSSC insists the operation policy of pursuing special,holds the philossophy of "I have what you haven't,I expertise what you have",and adhere to the "science and technology enterprises,human resources enterpises,independent creation"idea,and insist on the operation principle"people oriented".The company has gradually formed a corporate identity which is "superior production technology,self-contained specialized equipment,strong technology research and development,high technology content",and realized the strategic objectives to build PCSSC as a maijr military manufacturing base,the domestic first-class Titanium steel bounded type fine steel bases and nuclear power production base.

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:17-4PH