X7Cr14

Data Table for: Steel Grades : Stainless Steel : X7Cr14

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce X7Cr14 specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • X7Cr14
  • X7Cr14
  • X7Cr14
  • X7Cr14
  • X7Cr14
  • X7Cr14
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

 

Si 
Mn 
 P
 S
Cr   Ni  Mo  Other
 0.08  1.00  1.00  0.045  0.030  13.0-15.0      

 

Stainless Steel (Stainless Steel) refers to air, steam, water resistance and weak corrosive medium and acid, alkali, salt, chemical corrosion of Steel of erosion medium, also called Stainless Steel acid. In practical application, often be weak corrosive medium corrosion resistance of steel called stainless steel, and chemical resistance of medium corrosion of steel called acid steel. Because both in chemical composition, the gap between the former not resistant to corrosion medium chemistry, and the latter is normally has no rust sex. Stainless steel corrosion resistance depends on steel contain alloy element. Stainless steel alloy elements and basic nickel and molybdenum, titanium, niobium, copper, nitrogen etc, in order to meet various USES of the stainless steel organization and performance requirements.

 

The chemical composition of the stainless steel corrosion resistance with the increase of the carbon content and reduce, therefore, most of the carbon content of stainless steel were lower, some steel the wC (carbon) and even less than 0.03% (such as 00 Cr12). Stainless steel alloy element is the main, Cr, only when Cr content to a certain value, steel have corrosion resistance. Therefore, stainless steel general wCr were above 13%. Stainless steel with Ni, Ti, Mn, N, Nb the element.

 

Stainless steel used to the organization state is divided into: martensite steel, ferritic steel, austenitic steel, etc. In addition, the composition is divided into: chromium stainless steel, chromium nickel stainless steel and chromium manganese nitrogen stainless steel, etc.

 

1, ferritic stainless steel: including chromium 12% ~ 30%. The corrosion resistance and toughness and weldability with containing cr increases with the increasing of quantity, chloride stress corrosion resistance performance is better than other types of stainless steel.

 

 

Belong to this category of Crl7, Cr17Mo2Ti, have Cr25, Cr25Mo3Ti, Cr28, etc. Ferritic stainless steel because contain chromium volume is high, corrosion resistance and oxidation resistance are relatively good, but the mechanical properties and the process performance is poorer, more for stress of acid structure and as little antioxidant use steel. This kind of steel can resist the atmosphere, nitric acid and brine solution of the corrosion, and has high temperature oxidation resistance, good thermal expansion coefficient characteristics such as small, used to nitric acid and food factory equipment, also can make in the high temperature parts, such as gas turbine parts, etc.

 

2, austenitic stainless steel: including chromium greater than 18%, still contain 8% of nickel and a few molybdenum, titanium, nitrogen element. Comprehensive performance is good, resistant to a variety of medium corrosion. Austenitic stainless steel grades of commonly used one Cr18Ni9, 0 Cr19Ni9, etc. 0 Cr19Ni9 steel the wC < 0.08%, GangHao marked as "0". This kind of steel contain a lot of Ni and Cr, make steel at room temperature is austenitic state. This kind of steel has good plasticity and toughness, weldability and corrosion resistance, in oxidizing and reducing medium corrosion resistance were well, used to make acid equipment, such as corrosion resistant containers and equipment, pipeline, resistant to the lining of the equipment parts nitric acid. Austenitic stainless steel generally USES solid solution processing, steel is heated to a 1050 ~ 1150 ℃, and water, for single-phase austenitic organization.

 

3, austenitic-ferritic duplex stainless steel: with austenitic stainless steel and the advantages of ferrite, and has the plastic.

 

 

Austenitic and ferritic organization about half of the stainless steel. Containing C in the situation of low, Cr content at 18% ~ 28%, 3% ~ 10% in Ni content. Some steel also contain Mo, Cu, Si, Nb, Ti, N, alloy element. This kind of steel with austenitic stainless steel and the characteristics of ferrite, compared with ferrite, plastic, higher toughness, no room temperature brittleness, intergranular corrosion resistant performance and welding properties are improved significantly and also maintain a ferritic stainless steel 475 ℃ brittle and high thermal conductivity, and has the characteristics such as plastic. Compared with austenitic stainless steel, high strength and corrosion resistance and intergranular corrosion resistant to chloride stress have increased significantly. Duplex stainless steel has excellent resistance to corrosion resistance hole, is also a kind of festival nickel stainless steel.

 

4, martensite stainless steel, high strength, but plastic and solderability is poorer.

 

Martensite stainless steel grades of commonly used one Cr13, 3 Cr13 and so on, because it contains carbon is higher, it has high strength, hardness and wear resistance, corrosion resistance is a bit poor, mechanical performance requirements for higher, corrosion resistance performance of some parts of the general requirements, such as spring, turbine blade, hydraulic press valves, etc. This kind of steel is quenching and tempering treatment in use.


Company Instoduction:Sichuan Changcheng Special Steel Limited Liability
Company of Pan Steel Group(hereinafter referred to as PCSSC) Iocates in Jiangyou City,Sichuan Province,which former name is Changcheng Steel
Factory of Metallurgical Industry.It's built up in the year of 1965 and put into production in 1972.PCSSC has become one of the large core enterprises in Sichuan province and the important research and manufacture
base for special steel of China.In 1994,Changcheng special Steel Corporation ,the shareholding subsidiary of PCSSC has been listed on Shenzhen Stock Exchange.On June,2004,Pan steel Group reformed Changcheng Special Steel Company formally,and formed Sichuan Changcheng Special Steel
Limited Liability Company of Pan Steel Group.
At present,PCSSC has the annual production capacity to turn out 650,000
tons of special steel and 700,000 tons of finished steel products.It can supply users with 12 kinds of qualitative special steel and metal products
more than 350 grades,over 5000 dimensions on the international or national standard.The products can be widely used in all aspects of aviation,aerospace,shipbuilding,military industry,nuclear power and transportation,machine,petrochemical,medical instruments and so on.And sold to all of the country and exported into USA,Europe and Southeast Asia,etc.Some 34 products have awarded the title of the
National,Ministerial and Provincial level high-quality products.Also,product quality as cold-work mould steel has reached international level.After more than forty years development,PCSSC has grwn
into the important national special steel research and production base and military industry supporting enterprise and become irreplaceable imporyant force in the domains of national defense industry,aviation,aerospace,navigation and nuclear power.
Thereto,top-end products as titanium products and nuclear power tubes have strong market competitions and formed a new economic grow point.PCSSC is one of the three main military products and super alloyed steel production bases of China,which is on a par with the Northeast Special Steel and Special Steel of Bao Steel.It makes great contribution to insist
on self reliance,speed up national befense modern construction,to enhance our capability of independent innovation and insist on self-development to push forward nationalizing major equipment construction.
PCSSC insists the operation policy of pursuing special,holds the philossophy of "I have what you haven't,I expertise what you have",and adhere to the "science and technology enterprises,human resources enterpises,independent creation"idea,and insist on the operation principle"people oriented".The company has gradually formed a corporate identity which is "superior production technology,self-contained specialized equipment,strong technology research and development,high technology content",and realized the strategic objectives to build PCSSC as a maijr military manufacturing base,the domestic first-class Titanium steel bounded type fine steel bases and nuclear power production base.

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:X7Cr14

Previous pageX6Cr13
Next page:X6CrAl13