Q195

Data Table for: Steel Grades : Structure Steel : Q195

Chemical composition(mass fraction)(wt.%)

  • C
  • Si
  • Mn
  • P
  • S
  • Cr
  • Ni
  • 0.06~0.12
  • ≤0.30
  • 0.25~0.50
  • ≤0.045
  • ≤0.050
  • ≤0.30
  • ≤0.30
  • Cu
  • ≤0.30

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce Q195 specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • Q195
  • Q195
  • Q195
  • Q195
  • Q195
  • Q195
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

Engineering and welding

Mechanics performance


The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | ≤ 16:195
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 16 ~ 40:185

Tensile strength σ b/MPa: 315 ~ 430
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | than 16:33
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 16 ~ 40:32
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 40 to 60:-
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 60 ~ 100:-
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 100 ~ 150:-
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 150:-
Impact test (1) | temperature / ℃ :-
Impact test (1) | impact absorption power AKV/J:- 

Cold bending property


Sample direction: vertical
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | than 60:0
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | > 60 ~ 100:-
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | > 100 ~ 200:-

Performance characteristics and applications 


High plasticity and toughness and welding performance, good pressure processing performance, but low strength. 
Load small parts, spacers, rivets, the anchor bolt, colter, funnel, roof, low carbon steel wire, plates, welded pipe, bars, split cotters, and stamping parts, components etc. 

 

GB/T 700-1988 standard and GB 700-1979 standard steel grade comparison 

GB/T 700-1988 standadr:

Regardless of rank, the chemical composition and mechanical properties (σ s, σ b, the delta and the cold bending) are to be guaranteed

Rolling plate and rod of products, the mechanical properties of the guarantee condition, can according to product characteristics and application requirements, in the standard separately 

GB 700-1979 standard
 

A1 the mechanical properties of the steel guarantee (σ s, σ b, the delta and the cold bending), B1 steel guarantee the chemical composition of the same with Q195

A1 steel cold bending test is additional guarantee conditions

1 no special steel of steel

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:Q195

Previous pageFirst page
Next page:Q215