Home » Steel Grades > Structure Steel > Q235 B

Category

Contact us

Q235 B

Data Table for: Steel Grades : Structure Steel : Q235 B

Chemical composition(mass fraction)(wt.%)

  • C
  • Si
  • Mn
  • P
  • S
  • Cr
  • Ni
  • 0.12~0.20
  • ≤0.30
  • 0.30~0.70
  • ≤0.045
  • ≤0.045
  • ≤0.30
  • ≤0.30
  • Cu
  • ≤0.30

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce Q235 B specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • Q235 B
  • Q235 B
  • Q235 B
  • Q235 B
  • Q235 B
  • Q235 B
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

Engineering and welding

Mechanical properties

The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | ≤ 16:235
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 16 ~ 40:225
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 40 to 60:215
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 60 ~ 100:205
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 100 ~ 150:195
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 150:185


Tensile strength σ b/MPa: 375 ~ 450
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | than 16:26
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 16 ~ 40:25
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 40 to 60:24
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 60 ~ 100:23
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 100 ~ 150:22
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 150:21
Impact test (1) | temperature / ℃ : 20
Impact test (1) | impact absorption power AKV/J: 27 frequency 

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:Q235

Previous pageQ235
Next page:Q235 C