Contact us

Q275

Data Table for: Steel Grades : Structure Steel : Q275

Chemical composition(mass fraction)(wt.%)

  • C
  • Si
  • Mn
  • P
  • S
  • Cr
  • Ni
  • 0.28~0.38
  • ≤0.35
  • 0.50~0.80
  • ≤0.045
  • ≤0.050
  • ≤0.30
  • ≤0.30
  • Cu
  • ≤0.30

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce Q275 specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • Q275
  • Q275
  • Q275
  • Q275
  • Q275
  • Q275
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

Engineering and welding

Mechanical properties


The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | than 16:275
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 16 ~ 40:265
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 40 to 60:255
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 60 ~ 100:245
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 100 ~ 150:235
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 150:225

Tensile strength σ b/MPa: 490 ~ 630
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | than 16:20
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 16 ~ 40:19
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 40 to 60:18
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 60 ~ 100:17
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 100 ~ 150:16
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 150:15
Impact test (1) | temperature / ℃ :-
Impact test (1) | impact absorption power AKV/J:-

The cold bending property


Sample direction:-
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | than 60: d = 3 a
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | > 60 ~ 100: d = 4 a
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | > 100 ~ 200: d = 4.5 a

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:Q275

Previous pageQ255 B
Next page:Q235q C