ASTM B265 Gr1 Ti Alloy

Data Table for: Steel Grades : Ti Alloy : ASTM B265 Gr1 Ti Alloy

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce ASTM B265 Gr1 Ti Alloy specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • ASTM B265 Gr1 Ti Alloy
  • ASTM B265 Gr1 Ti Alloy
  • ASTM B265 Gr1 Ti Alloy
  • ASTM B265 Gr1 Ti Alloy
  • ASTM B265 Gr1 Ti Alloy
  • ASTM B265 Gr1 Ti Alloy
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

ASTM B265 Gr1 Ti Alloy

Our advantages

ASTM B265 Gr1 properties and heat treatment forged piece, Including ASTM B265 Gr1 application and specifications, We have all specifications,Including ASTM B265 Gr1 steel plate, ASTM B265 Gr1 sheet, ASTM B265 Gr1 square steel, ASTM B265 Gr1 flat bar,ASTM B265 Gr1 round bar,ASTM B265 Gr1 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM B265 Gr1 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM B265 Gr1 and Standards

230.4~60mm
 

Brief description:

Titanium sheet/plate

Specification: T(0.4-60mm)*WT(400-3000mm)*L(1000-3000mm)

Material: Gr1 Gr2 Gr3 Gr4 Gr5 Gr7 Gr9 Gr12 Gr23

Standard: ASTM B265 BSW AMS JIS ISO9001:2000

Detailed description:

Titanium sheet/plate, titanium alloy sheet, mirror surface titanium sheet, titanium clad sheet

CP grade 1 can be used in the deep drawing parts for its good elongation and excellent corrosion-resistance.

CP grade 2 is used the most widely in the commercially pure titanium.

CP grade 3 is almost only used in pressure vessel.

CP grade 4 can be use in some fittings parts and fastening pieces, but for complex shape need 300 degree celsius to form.

Alloy grade 5, Ti-6Al-4V, is the most widely used in the titanium alloys because of its comprehensive mechanical, physical and chemical properties.

Alloy grade 7, add little palladium in cp titanium and it has the most excellent corrosion-resistance. Of course it costs higher.

Alloy grade 9, Ti-3Al-2.5V, is the most widely used in the golf clubs and bicycle girders.

Alloy grade 12, it has the similar properties with the grade 7 but costs lesser.

Alloy grade 23, Ti-6Al-4V ELI (Extra Low Interstitial) can be use in the medical appliance

 

Mark

Production method

Processing technical

Standard

TA1(GR1) TA2(GR2)

TA9(GR7)

TC4(GR5)

TA18(GR9)

TC4ELI(GR23)

Hot rolled

R&M

CB/T3621-94   GB/T14845-2007

Y&M

ASTM B265  ASTM F67  ASTM F136  MIL

Cold rolled

C

BWS

C

JIS




Machining performance

Download ASTM B265 Gr1 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:ASTM B265 Gr1 steel plate, ASTM B265 Gr1 sheet, ASTM B265 Gr1 square steel, ASTM B265 Gr1 flat bar,ASTM B265 Gr1 round bar,ASTM B265 Gr1 forgings


 

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:ASTM B265

Previous pageTA1ELI Ti Alloy
Next page:DIN 1.1167 Ti Alloy