ASTM F1295 Ti Alloy

Data Table for: Steel Grades : Ti Alloy : ASTM F1295 Ti Alloy

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce ASTM F1295 Ti Alloy specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • ASTM F1295 Ti Alloy
  • ASTM F1295 Ti Alloy
  • ASTM F1295 Ti Alloy
  • ASTM F1295 Ti Alloy
  • ASTM F1295 Ti Alloy
  • ASTM F1295 Ti Alloy
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyASTM F1295 plate,ASTM F1295 Round Bar,ASTM F1295 forgings,ASTM F1295 suppliers, ASTM F1295 Stock,ASTM F1295 sheet, ASTM F1295 flat bar, ASTM F1295 pipe,ASTM F1295 tube,ASTM F1295 mould,ASTM F1295 round ingot,ASTM F1295 cold-rolled steel,ASTM F1295 coil,ASTM F1295 strap steel,ASTM F1295 hot-rolled steel,ASTM F1295 medium plate, ASTM F1295 heavy plate,ASTM F1295 shapped bar,ASTM F1295 hexahedral bar,ASTM F1295,ASTM F1295 slab ingot,ASTM F1295 slab,ASTM F1295 price,ASTM F1295 square bar,ASTM F1295 square steel,ASTM F1295 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM F1295.

ASTM F1295 Ti Alloy

Our advantages

ASTM F1295 properties and heat treatment forged piece, Including ASTM F1295 application and specifications, We have all specifications,Including ASTM F1295 steel plate, ASTM F1295 sheet, ASTM F1295 square steel, ASTM F1295 flat bar,ASTM F1295 round bar,ASTM F1295 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM F1295 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM F1295 and Standards

 

Ti6Al7Nb ASTM F1295
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Beta Titanium Alloy
Key Words: medical, surgical

 

 

Physical Properties Metric English Comments
Density 4.52 g/cc 0.163 lb/in³
 
Mechanical Properties Metric English Comments
Modulus of Elasticity 110 GPa 16000 ksi
 
Thermal Properties Metric English Comments
Transformation Temperature 995 - 1025 °C 1820 - 1877 °F
 
Component Elements Properties Metric English Comments
Aluminum, Al 5.50 - 6.50 % 5.50 - 6.50 %
Carbon, C 0.080 % 0.080 %
Hydrogen, H 0.0090 % 0.0090 %
Iron, Fe 0.25 % 0.25 %
Niobium, Nb (Columbium, Cb) 6.50 - 7.50 % 6.50 - 7.50 %
Nitrogen, N 0.050 % 0.050 %
Oxygen, O 0.20 % 0.20 %
Tantalum, Ta 0.50 % 0.50 %
Titanium, Ti 84.911 - 86.911 % 84.911 - 86.911 %
 
Descriptive Properties
Microstructure Al-A9
Phase at room temp a+ß

 

Users viewing this material also viewed the following:
Ti5Al2.5Fe ISO 5832/X
Overview of materials for Alpha/Beta Titanium Alloy
Overview of materials for 7000 Series Aluminum Alloy
Titanium, Ti
Titanium Ti-6Al-4V ELI (Grade 23), Annealed

MMEDIC25 / 12401




Machining performance

Download ASTM F1295 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:ASTM F1295 steel plate, ASTM F1295 sheet, ASTM F1295 square steel, ASTM F1295 flat bar,ASTM F1295 round bar,ASTM F1295 forgings

 
 

关闭提示 关闭

 

确 认 取 消

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:ASTM F1295

Previous pageTi6Al7Nb Ti Alloy
Next page:Ti5Al2.5Fe Ti Alloy