Ti-2.5Al-1Mo-1V-1-5Zr Ti Alloy

Data Table for: Steel Grades : Ti Alloy : Ti-2.5Al-1Mo-1V-1-5Zr Ti Alloy

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce Ti-2.5Al-1Mo-1V-1-5Zr Ti Alloy specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • Ti-2.5Al-1Mo-1V-1-5Zr Ti Alloy
  • Ti-2.5Al-1Mo-1V-1-5Zr Ti Alloy
  • Ti-2.5Al-1Mo-1V-1-5Zr Ti Alloy
  • Ti-2.5Al-1Mo-1V-1-5Zr Ti Alloy
  • Ti-2.5Al-1Mo-1V-1-5Zr Ti Alloy
  • Ti-2.5Al-1Mo-1V-1-5Zr Ti Alloy
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

 

 

 

Ti-2.5Al-1Mo-1V-1-5Zr Ti Alloy

Our advantages

Ti-2.5Al-1Mo-1V-1-5Zr properties and heat treatment forged piece, Including Ti-2.5Al-1Mo-1V-1-5Zr application and specifications, We have all specifications,Including Ti-2.5Al-1Mo-1V-1-5Zr steel plate, Ti-2.5Al-1Mo-1V-1-5Zr sheet, Ti-2.5Al-1Mo-1V-1-5Zr square steel, Ti-2.5Al-1Mo-1V-1-5Zr flat bar,Ti-2.5Al-1Mo-1V-1-5Zr round bar,Ti-2.5Al-1Mo-1V-1-5Zr forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti-2.5Al-1Mo-1V-1-5Zr has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti-2.5Al-1Mo-1V-1-5Zr and Standards

 

Chemical composition,%
Main ingredients
Impurities,Not more than
Ti
Al
Sn
Mo
V
Mn
Zr
Si
Nd
Fe
C
N
H
O
other
only
sum
 
2.0~3.0
 
0.5~1.5
0.5~1.5
 
1.0~2.0
≤0.10
 
0.15
0.05
0.04
0.003
0.12
0.10
0.30

 




Machining performance

Download Ti-2.5Al-1Mo-1V-1-5Zr the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti-2.5Al-1Mo-1V-1-5Zr steel plate, Ti-2.5Al-1Mo-1V-1-5Zr sheet, Ti-2.5Al-1Mo-1V-1-5Zr square steel, Ti-2.5Al-1Mo-1V-1-5Zr flat bar,Ti-2.5Al-1Mo-1V-1-5Zr round bar,Ti-2.5Al-1Mo-1V-1-5Zr forgings

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:Ti-2.5Al-1Mo-1V-1-5Zr Ti

Previous pageTi-2Al-2-5Zr Ti Alloy
Next page:Ti-6.5Al-1Mo-1V-2Zr Ti Alloy