Ti-4AI-4Mo-2Sn Ti Alloy

Data Table for: Steel Grades : Ti Alloy : Ti-4AI-4Mo-2Sn Ti Alloy

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce Ti-4AI-4Mo-2Sn Ti Alloy specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • Ti-4AI-4Mo-2Sn Ti Alloy
  • Ti-4AI-4Mo-2Sn Ti Alloy
  • Ti-4AI-4Mo-2Sn Ti Alloy
  • Ti-4AI-4Mo-2Sn Ti Alloy
  • Ti-4AI-4Mo-2Sn Ti Alloy
  • Ti-4AI-4Mo-2Sn Ti Alloy
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi-4AI-4Mo-2Sn plate,Ti-4AI-4Mo-2Sn Round Bar,Ti-4AI-4Mo-2Sn forgings,Ti-4AI-4Mo-2Sn suppliers, Ti-4AI-4Mo-2Sn Stock,Ti-4AI-4Mo-2Sn sheet, Ti-4AI-4Mo-2Sn flat bar, Ti-4AI-4Mo-2Sn pipe,Ti-4AI-4Mo-2Sn tube,Ti-4AI-4Mo-2Sn mould,Ti-4AI-4Mo-2Sn round ingot,Ti-4AI-4Mo-2Sn cold-rolled steel,Ti-4AI-4Mo-2Sn coil,Ti-4AI-4Mo-2Sn strap steel,Ti-4AI-4Mo-2Sn hot-rolled steel,Ti-4AI-4Mo-2Sn medium plate, Ti-4AI-4Mo-2Sn heavy plate,Ti-4AI-4Mo-2Sn shapped bar,Ti-4AI-4Mo-2Sn hexahedral bar,Ti-4AI-4Mo-2Sn,Ti-4AI-4Mo-2Sn slab ingot,Ti-4AI-4Mo-2Sn slab,Ti-4AI-4Mo-2Sn price,Ti-4AI-4Mo-2Sn square bar,Ti-4AI-4Mo-2Sn square steel,Ti-4AI-4Mo-2Sn wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti-4AI-4Mo-2Sn.

Ti-4AI-4Mo-2Sn Ti Alloy

Our advantages

Ti-4AI-4Mo-2Sn properties and heat treatment forged piece, Including Ti-4AI-4Mo-2Sn application and specifications, We have all specifications,Including Ti-4AI-4Mo-2Sn steel plate, Ti-4AI-4Mo-2Sn sheet, Ti-4AI-4Mo-2Sn square steel, Ti-4AI-4Mo-2Sn flat bar,Ti-4AI-4Mo-2Sn round bar,Ti-4AI-4Mo-2Sn forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti-4AI-4Mo-2Sn has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti-4AI-4Mo-2Sn and Standards

Ti-4AI-4Mo-2Sn




Machining performance

Download Ti-4AI-4Mo-2Sn the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti-4AI-4Mo-2Sn steel plate, Ti-4AI-4Mo-2Sn sheet, Ti-4AI-4Mo-2Sn square steel, Ti-4AI-4Mo-2Sn flat bar,Ti-4AI-4Mo-2Sn round bar,Ti-4AI-4Mo-2Sn forgings

 
 

关闭提示 关闭

 

确 认 取 消

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader