Ti-6Al-4V-ELI (low O2) Ti Alloy

Data Table for: Steel Grades : Ti Alloy : Ti-6Al-4V-ELI (low O2) Ti Alloy

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce Ti-6Al-4V-ELI (low O2) Ti Alloy specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • Ti-6Al-4V-ELI (low O2) Ti Alloy
  • Ti-6Al-4V-ELI (low O2) Ti Alloy
  • Ti-6Al-4V-ELI (low O2) Ti Alloy
  • Ti-6Al-4V-ELI (low O2) Ti Alloy
  • Ti-6Al-4V-ELI (low O2) Ti Alloy
  • Ti-6Al-4V-ELI (low O2) Ti Alloy
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

Ti-6Al-4V-ELI (low O2) Ti Alloy

Our advantages

Ti-6Al-4V-ELI (low O2) properties and heat treatment forged piece, Including Ti-6Al-4V-ELI (low O2) application and specifications, We have all specifications,Including Ti-6Al-4V-ELI (low O2) steel plate, Ti-6Al-4V-ELI (low O2) sheet, Ti-6Al-4V-ELI (low O2) square steel, Ti-6Al-4V-ELI (low O2) flat bar,Ti-6Al-4V-ELI (low O2) round bar,Ti-6Al-4V-ELI (low O2) forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti-6Al-4V-ELI (low O2) has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti-6Al-4V-ELI (low O2) and Standards

 

Category Titanium Alloy
Class Wrought
Type Alpha-beta alloy
Designations United States: MIL-T-9046, MIL-T-9047, AMS 4930, AMS 4907, AMS 4956
Composition
Element Weight %
Al  6 
V  4 

 

Mechanical Properties
Properties  Conditions
T (°C) Treatment
Density (×1000 kg/m3) 4.43 25  
Poisson's Ratio 0.342 25  
Elastic Modulus (GPa) 113.8 25  
Tensile Strength (Mpa) 896 25 annealed  
Yield Strength (Mpa) 827
Elongation (%) 15 
Reduction in Area (%) 35 
Hardness (HRC) 35  25 annealed 
Impact Strength (J)
(Charpy)
24 25 annealed  

 

Thermal Properties
Properties  Conditions
T (°C) Treatment
Thermal Expansion (10-6/ºC) 8.6 20-100 more  



Machining performance

Download Ti-6Al-4V-ELI (low O2) the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti-6Al-4V-ELI (low O2) steel plate, Ti-6Al-4V-ELI (low O2) sheet, Ti-6Al-4V-ELI (low O2) square steel, Ti-6Al-4V-ELI (low O2) flat bar,Ti-6Al-4V-ELI (low O2) round bar,Ti-6Al-4V-ELI (low O2) forgings


 

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:Ti-6Al-4V-ELI (

Previous pageTi-6Al-6V-2Sn-0.75Cu Ti Alloy
Next page:Ti-6Al-4V Ti Alloy