Ti12Mo5Zr5Sn Ti Alloy

Data Table for: Steel Grades : Ti Alloy : Ti12Mo5Zr5Sn Ti Alloy

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce Ti12Mo5Zr5Sn Ti Alloy specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • Ti12Mo5Zr5Sn Ti Alloy
  • Ti12Mo5Zr5Sn Ti Alloy
  • Ti12Mo5Zr5Sn Ti Alloy
  • Ti12Mo5Zr5Sn Ti Alloy
  • Ti12Mo5Zr5Sn Ti Alloy
  • Ti12Mo5Zr5Sn Ti Alloy
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi12Mo5Zr5Sn plate,Ti12Mo5Zr5Sn Round Bar,Ti12Mo5Zr5Sn forgings,Ti12Mo5Zr5Sn suppliers, Ti12Mo5Zr5Sn Stock,Ti12Mo5Zr5Sn sheet, Ti12Mo5Zr5Sn flat bar, Ti12Mo5Zr5Sn pipe,Ti12Mo5Zr5Sn tube,Ti12Mo5Zr5Sn mould,Ti12Mo5Zr5Sn round ingot,Ti12Mo5Zr5Sn cold-rolled steel,Ti12Mo5Zr5Sn coil,Ti12Mo5Zr5Sn strap steel,Ti12Mo5Zr5Sn hot-rolled steel,Ti12Mo5Zr5Sn medium plate, Ti12Mo5Zr5Sn heavy plate,Ti12Mo5Zr5Sn shapped bar,Ti12Mo5Zr5Sn hexahedral bar,Ti12Mo5Zr5Sn,Ti12Mo5Zr5Sn slab ingot,Ti12Mo5Zr5Sn slab,Ti12Mo5Zr5Sn price,Ti12Mo5Zr5Sn square bar,Ti12Mo5Zr5Sn square steel,Ti12Mo5Zr5Sn wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti12Mo5Zr5Sn.

 

Ti12Mo5Zr5Sn Ti Alloy

Our advantages

Ti12Mo5Zr5Sn properties and heat treatment forged piece, Including Ti12Mo5Zr5Sn application and specifications, We have all specifications,Including Ti12Mo5Zr5Sn steel plate, Ti12Mo5Zr5Sn sheet, Ti12Mo5Zr5Sn square steel, Ti12Mo5Zr5Sn flat bar,Ti12Mo5Zr5Sn round bar,Ti12Mo5Zr5Sn forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti12Mo5Zr5Sn has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti12Mo5Zr5Sn and Standards

Ti12Mo5Zr5Sn ß titanium alloy
Categories: Metal; Nonferrous Metal; Titanium Alloy; Beta Titanium Alloy

Key Words: medical, surgical

 

Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1010 MPa 146000 psi as forged and aged (600°C)
Tensile Strength, Yield 1002 MPa 145300 psi as forged and aged (600°C)
Elongation at Break 17.8 % 17.8 % as forged and aged (600°C)
Reduction of Area 56.0 % 56.0 % as forged and aged (600°C)
 
Component Elements Properties Metric English Comments
Molybdenum, Mo 11.5 % 11.5 %
Tin, Sn 4.50 % 4.50 %
Titanium, Ti 79.0 % 79.0 %
Zirconium, Zr 5.0 % 5.0 %

 

Users viewing this material also viewed the following:
Ti15Mo5Zr3Al ß titanium alloy
Ti30Nb ß titanium alloy
Ti30Ta ß titanium alloy
Ti5Al2.5Fe ISO 5832/X
Ti6Al7Nb ASTM F1295

MMEDIC27 / 12403




Machining performance

Download Ti12Mo5Zr5Sn the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti12Mo5Zr5Sn steel plate, Ti12Mo5Zr5Sn sheet, Ti12Mo5Zr5Sn square steel, Ti12Mo5Zr5Sn flat bar,Ti12Mo5Zr5Sn round bar,Ti12Mo5Zr5Sn forgings

 
 

关闭提示 关闭

 

确 认 取 消

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:Ti12Mo5Zr5Sn Ti

Previous pageTi30Nb Ti Alloy
Next page:Ti15Mo5Zr3Al Ti Alloy