Home » Steel Grades > Ti Alloy > Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy

Category

Contact us

Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy

Data Table for: Steel Grades : Ti Alloy : Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy
  • Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy
  • Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy
  • Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy
  • Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy
  • Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi-6Al-2Nb-1Ta-0.8Mo plate,Ti-6Al-2Nb-1Ta-0.8Mo Round Bar,Ti-6Al-2Nb-1Ta-0.8Mo forgings,Ti-6Al-2Nb-1Ta-0.8Mo suppliers, Ti-6Al-2Nb-1Ta-0.8Mo Stock,Ti-6Al-2Nb-1Ta-0.8Mo sheet, Ti-6Al-2Nb-1Ta-0.8Mo flat bar, Ti-6Al-2Nb-1Ta-0.8Mo pipe,Ti-6Al-2Nb-1Ta-0.8Mo tube,Ti-6Al-2Nb-1Ta-0.8Mo mould,Ti-6Al-2Nb-1Ta-0.8Mo round ingot,Ti-6Al-2Nb-1Ta-0.8Mo cold-rolled steel,Ti-6Al-2Nb-1Ta-0.8Mo coil,Ti-6Al-2Nb-1Ta-0.8Mo strap steel,Ti-6Al-2Nb-1Ta-0.8Mo hot-rolled steel,Ti-6Al-2Nb-1Ta-0.8Mo medium plate, Ti-6Al-2Nb-1Ta-0.8Mo heavy plate,Ti-6Al-2Nb-1Ta-0.8Mo shapped bar,Ti-6Al-2Nb-1Ta-0.8Mo hexahedral bar,Ti-6Al-2Nb-1Ta-0.8Mo,Ti-6Al-2Nb-1Ta-0.8Mo slab ingot,Ti-6Al-2Nb-1Ta-0.8Mo slab,Ti-6Al-2Nb-1Ta-0.8Mo price,Ti-6Al-2Nb-1Ta-0.8Mo square bar,Ti-6Al-2Nb-1Ta-0.8Mo square steel,Ti-6Al-2Nb-1Ta-0.8Mo wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti-6Al-2Nb-1Ta-0.8Mo.

 

Ti-6Al-2Nb-1Ta-0.8Mo Ti Alloy

Our advantages

Ti-6Al-2Nb-1Ta-0.8Mo properties and heat treatment forged piece, Including Ti-6Al-2Nb-1Ta-0.8Mo application and specifications, We have all specifications,Including Ti-6Al-2Nb-1Ta-0.8Mo steel plate, Ti-6Al-2Nb-1Ta-0.8Mo sheet, Ti-6Al-2Nb-1Ta-0.8Mo square steel, Ti-6Al-2Nb-1Ta-0.8Mo flat bar,Ti-6Al-2Nb-1Ta-0.8Mo round bar,Ti-6Al-2Nb-1Ta-0.8Mo forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti-6Al-2Nb-1Ta-0.8Mo has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti-6Al-2Nb-1Ta-0.8Mo and Standards

 

Titanium Ti-6Al-2Nb-1Ta-0.8Mo (Ti-621/0.8), as-rolled
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy
Material Notes: As-rolled from above Beta Transus. Alpha Alloy.
3 other heat treatments of this alloy are in MatWeb.
Key Words: Ti-621/0.8; UNS R56210; Ti-6211

 

 

Physical Properties Metric English Comments
Density 4.48 g/cc 0.162 lb/in³
 
Mechanical Properties Metric English Comments
Hardness, Brinell 290 290 Estimated from Rockwell C.
Hardness, Knoop 315 315 Estimated from Rockwell C.
Hardness, Rockwell C 30 30
Hardness, Vickers 304 304 Estimated from Rockwell C.
Tensile Strength, Ultimate 830 MPa 120000 psi
Tensile Strength, Yield 760 MPa 110000 psi
Elongation at Break 10.0 % 10.0 %
Reduction of Area 28.0 % 28.0 % Average of Longitudinal and Transverse
Modulus of Elasticity 117 GPa 17000 ksi In Tension
Compressive Yield Strength 820 MPa 119000 psi
Compressive Modulus 126 GPa 18300 ksi
Poissons Ratio 0.310 0.310
Charpy Impact 37.0 J 27.3 ft-lb V-notch
Shear Modulus 44.7 GPa 6480 ksi Calculated
 
Electrical Properties Metric English Comments
Electrical Resistivity 0.000160 ohm-cm 0.000160 ohm-cm
 
Thermal Properties Metric English Comments
CTE, linear 9.00 µm/m-°C
@Temperature 20.0 - 650 °C
5.00 µin/in-°F
@Temperature 68.0 - 1200 °F
average
  9.20 µm/m-°C
@Temperature 20.0 - 93.0 °C
5.11 µin/in-°F
@Temperature 68.0 - 199 °F
annealed
Specific Heat Capacity 0.552 J/g-°C 0.132 BTU/lb-°F
Thermal Conductivity 6.40 W/m-K 44.4 BTU-in/hr-ft²-°F
Melting Point <= 1650 °C <= 3000 °F Liquidus
Liquidus 1650 °C 3000 °F
Beta Transus 1110 °C 2030 °F
 
Component Elements Properties Metric English Comments
Aluminum, Al 6.0 % 6.0 %
Molybdenum, Mo 0.80 % 0.80 %
Niobium, Nb (Columbium, Cb) 2.0 % 2.0 %
Tantalum, Ta 1.0 % 1.0 %
Titanium, Ti 90.0 % 90.0 %

 

Users viewing this material also viewed the following:
Titanium Ti-6Al-2Sn-4Zr-2Mo-0.1Si; Duplex Annealed
Titanium Ti-6Al-2Nb-1Ta-0.8Mo (Ti-621/0.8), Alpha-Annealed
Titanium 11 (Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si)
Titanium Ti-6Al-2Nb-1Ta-0.8Mo (Ti-621/0.8), STA-1
Titanium Ti-6Al-2Nb-1Ta-1Mo

MTA181 / 14117




Machining performance

Download Ti-6Al-2Nb-1Ta-0.8Mo the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti-6Al-2Nb-1Ta-0.8Mo steel plate, Ti-6Al-2Nb-1Ta-0.8Mo sheet, Ti-6Al-2Nb-1Ta-0.8Mo square steel, Ti-6Al-2Nb-1Ta-0.8Mo flat bar,Ti-6Al-2Nb-1Ta-0.8Mo round bar,Ti-6Al-2Nb-1Ta-0.8Mo forgings

 
 

关闭提示 关闭

 

确 认 取 消

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:Ti-6Al-2Nb-1Ta-0.8Mo Ti

Previous pageTi-621/0.8 Ti Alloy
Next page:Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy