Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy

Data Table for: Steel Grades : Ti Alloy : Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy

Chemical composition(mass fraction)(wt.%)

Mechanical Properties

  • Quantity
  • Value
  • Unit
  • Young's modulus
  • Tensile strength
  • Elongation
  • Fatigue
  • Yield strength
  • 200000 - 200000
  • 650 - 880
  • 8 - 25
  • 275 - 275
  • 350 - 550
  • MPa
  • MPa
  • %
  • MPa
  • MPa

Physical Properties

  • Quantity
  • Value
  • Unit
  • Thermal expansion
  • Thermal conductivity
  • Specific heat
  • Melting temperature
  • Density
  • Resistivity
  • 10 - 10
  • 25 - 25
  • 460 - 460
  • 1450 - 1510
  • 7700 - 7700
  • 0.55 - 0.55
  • e-6/K
  • W/m.K
  • J/kg.K
  • °C
  • kg/m3
  • Ohm.mm2/m

Heat Treatment:

Annealing

Quenching

Tempering

Normalizing

Q & T

Can produce Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy specifications and size

  • Steel grade
  • Specification
  • Processing range(mm)
  • Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy
  • Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy
  • Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy
  • Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy
  • Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy
  • Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy
  • Φ1 to Φ2000
  • 10 to 1000
  • 0.08 to 800(T)*10 to 1500(W)*Long
  • Pipe/tube/slugs/donuts/cubes/other shapes
  • OD: Φ4-410; WT: 1-35 mm
  • THK:0.1mm Width:1500mm

Description

 

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si plate,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Round Bar,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si forgings,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si suppliers, Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Stock,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si sheet, Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si flat bar, Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si pipe,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si tube,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si mould,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si round ingot,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si cold-rolled steel,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si coil,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si strap steel,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si hot-rolled steel,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si medium plate, Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si heavy plate,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si shapped bar,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si hexahedral bar,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si slab ingot,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si slab,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si price,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si square bar,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si square steel,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si.

Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Ti Alloy

Our advantages

Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si properties and heat treatment forged piece, Including Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si application and specifications, We have all specifications,Including Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si steel plate, Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si sheet, Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si square steel, Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si flat bar,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si round bar,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si and Standards

Titanium 11 (Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si)

Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy

Material Notes: 1 other heat treatment of this alloy is in MatWeb.

 

Physical Properties Metric English Comments
Density 4.50 g/cc 0.163 lb/in³
 
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1030 MPa 149000 psi
Tensile Strength, Yield 930 MPa 135000 psi
Elongation at Break 16.0 % 16.0 %
Reduction of Area 34.0 % 34.0 %
Modulus of Elasticity 115 GPa 16700 ksi Typical value for an alpha titanium alloy
Poissons Ratio 0.310 0.310 Typical for alpha titanium alloy.
Shear Modulus 43.9 GPa 6370 ksi Calculated from typical values.
 
Electrical Properties Metric English Comments
Electrical Resistivity 0.000160 ohm-cm 0.000160 ohm-cm Estimated from similar alpha titanium alloys.
 
Thermal Properties Metric English Comments
CTE, linear 9.00 µm/m-°C
@Temperature 20.0 - 100 °C
5.00 µin/in-°F
@Temperature 68.0 - 212 °F
Typical alpha titanium alloy
Specific Heat Capacity 0.525 J/g-°C 0.125 BTU/lb-°F Typical value for titanium alloys.
Thermal Conductivity 7.00 W/m-K 48.6 BTU-in/hr-ft²-°F Estimated from similar titanium alloys.
Beta Transus 980 - 1015 °C 1800 - 1859 °F
 
Component Elements Properties Metric English Comments
Aluminum, Al 6.0 % 6.0 %
Bismuth, Bi 0.35 % 0.35 %
Molybdenum, Mo 1.0 % 1.0 %
Silicon, Si 0.10 % 0.10 %
Tin, Sn 2.50 % 2.50 %
Titanium, Ti 89.0 % 89.0 %
Zirconium, Zr 1.50 % 1.50 %

 

Users viewing this material also viewed the following:
Titanium Ti-6Al-2Sn-4Zr-2Mo-0.1Si; Duplex Annealed
Titanium 11 (Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si), Aged
Titanium Ti-6Al-2Nb-1Ta-0.8Mo (Ti-621/0.8), as-rolled
Titanium, Ti
Titanium Ti-6Al-2Nb-1Ta-0.8Mo (Ti-621/0.8), STA-1

MTA110 / 14115




Machining performance

Download Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si steel plate, Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si sheet, Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si square steel, Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si flat bar,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si round bar,Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si forgings

 
 

关闭提示 关闭

 

确 认 取 消

Standard download

More standard download >>

Click the Get Adobe Reader button to download the Adobe Reader:

Download Adobe Reader

Download Adobe Reader

Related steel grade search:Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si Ti

Previous pageTi-6Al-2Nb-1Ta-0.8Mo Ti Alloy
Next page:Ti-6Al-2Sn-4Zr-2Mo-0-1Si Ti Alloy